refractory garde white aluminum oxide 3-5mm

We are a professional manufacture of white fused alumina since 1999. White fused alumina is a high-quality raw material, made of fused refining crystal, high purity, self-sharpening, good acid and alkali resistance, high temperature, thermal properties and stability. it is slightly higher than the corundum hardness, toughness slightly lower, high purity, good self-sharpening, grinding ability, heat, high efficiency, acid corrosion, high temperature thermal stability. Made with the abrasive, for grinding high-carbon copper, high-speed steel.

 Size we offer :

 Sand: 50-30mm,30-10mm,10-8mm,8-5mm, 5-3mm, 3-1mm, 0-1mm

 Fines: -320mesh-0, -280mesh-0, -240mesh-0, -200mesh-0, -180mesh-0,-100mesh-0

 Grain: F8, F10, F12, F14, F16, F20, F22, F24, F30, F36, F40, F46, F54,

            F60, F70, F80, F90, F100, F120, F150, F180, F220

Micron Powder: F240, F280, F320, F360, F400, F500, F600, F800, F1000, F1200 

The advantages and technical for white fused alumina/WFA as follows:

1.A manufacturer with 13 years professional experience in China.

2.Commissary company of the national technical standardization committee of abrasives.

3.High purity of 99.5% min.

4.Prompt delivery: within 5days after the receipt of the order.

5 Competitive and reasonable price.

2.Chemical and physical parameters

Chemical compositions

Al2O3 : 99.6

Na2O : 0.22

SiO2 : 0.10

Fe2O3: 0.04

Physical properties

Linear expansion coefficient(1/°C): 8.3x10-4

Morse hardness 9min

Grain density :3.9 g/cm3

Bulk density:1.75-1.95 g/cm3

White fused alumina abrasives sandblasting

Performance and advantages

1. Not affecting the color of the processing cases;

2. Sandblasting in the non-iron process;

3. High speed processing and quality;4.Containing a very low amount of iron oxide, suitable for non-ferrous blasting operations;5.After acid washing steps.

Usage:

1. Available research in a variety of blasting and light(lapping)operations;

2. Bolero or spay acrylic art of beauty processing;

3. The process of blasting the TV screen;

4. The cutting of silicon water;

5. The tooth model of clean sand;

6. Precision sand casting;

7. High refractory and other ceramic additives